3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: [email protected] or [email protected]
There are CAD communities available at: [email protected] or [email protected]
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
Be respectful, especially when disagreeing. Everyone should feel welcome here.
No porn (NSFW prints are acceptable but must be marked NSFW)
No Ads / Spamming / Guerrilla Marketing
Do not create links to reddit
If you see an issue please flag it
No guns
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
This is the temp tower of my wood print experiment Cand even se much difference. It goes from 260 to 190. Below 225 gets really flimsy and above 240 melts. But even 230, the "best" one is really bad, and I'm not talking about retraction. Even the layers that melt are inconsistent.
Also it's not humidity since the filament was in a filament dryer for.16hours.
edit: The nozzle is 0.8
can someone think of anything else?
This is how my wood PLA+ prints used to look too. Your extruder is almost 100% the issue. These filaments are spongy and don't extrude well. Try toying with your extruder tension and if that fails get a BMG knockoff
I thought so! My extruder was never good. Thanks I'll look at a bmg
Did you change the nozzle setting in your slicer to 0.8? They usually default to 0.4
It definitely looks under extruded.
Looks like a partial clog and too fast at the same time. A .8 nozzle lets a lot of material flow, try slowing down after checking for a clog.
Oh and are you skipping steps?
Yeah that immediately looks way under-extruded to me.
Also that wood stuff (from what I read) clogs terribly.
Yes that's why I'm using a .8 nozzle lol